Relation Casting: Ductile cast Iron Casting,Nodular cast iron casting

Ductile iron casting as found wide acceptance and competes favourably with steel such that its use in engineering has increased in recent times as while grey cast iron and malleable cast iron has fallen in popularity as other materials such as plastics have found favour.

Ductile iron casting has a clear advantage over malleable iron for applications where low solidification shrinkage is needed or where the section is too thick to permit uniform solidification as white iron

EQUIVALENT STANDARDS TECHNICAL SPECIFICATIONS
EN 1563	Germany	France	England	Netherlands	Sweden	USA		Hardness	Tensile Strength	0,2 Proof Stress	Elonga tion	Machinability	Microstructure
	DIN 1693	NF	BS	NEN	MNC	ASTM A536		HB	Rm N/mm/font>	Rp0,2 N/mm/font>	A5 %
EN-GJS-400- 18-LT	GGG-40.3		-	-	-	60-40-18		120-165	400-450	250-300	27-18	very good	Ferrit
EN-GJS-400-15	GGG-40	FGS 400-12	420/12	GN 42	0717-02	60-40-18		135-185	400-550	250-350	27-15	very good	Ferrit and Perlit
EN-GJS-450-10	-	-	420/12	-	-	65-45-12		160-210	450-600	310-410	20-10	good	Ferrit and Perlit
EN-GJS-500-7	GGG-50	FGS 500-7	500/7	GN 50	0727-02	65-45-12/ 80-55-06		170-220	500-650	320-420	18-7	good	Ferrit and Perlit
EN-GJS-600-3	GGG-60	FGS 600-3	600/3	GN 60	0732-03	80-55-06		200-250	600-750	370-480	8-3	good	Ferrit and Perlit
EN-GJS-700-2	GGG-70	FGS 700-2	700/2	GN 70	0737-01	100-70-03		235-285	700-850	420-600	6-2	moderate	Ferrit and Perlit
EN-GJS-800-2	GGG-80	FGS 800-2	800/2	-	-	120-90-02		270-335	800-1000	480-750	4-2	moderate	Perlit